| Study on Thermal Properties and Thermal Decomposition Mechanism of Hyperbranched Polyurethane Acrylate by TG-FTIR |
| |
| View Full Text Download reader |
| DOI： |
| KeyWord:TG-FTIR hyperbranched polyurethane acrylate Tg thermal decomposition mechanism |
| Author | Institution |
| SUN Ning，CHEN Chan，FENG Chun-yun，LI Yi-biao* |
1.五邑大学化学与环境工程学院;2.江门职业技术学院 |
|
| Hits: 2358 |
| Download times: 1202 |
| Abstract: |
| The thermo-gravimetric behaviors under different atmosphere and glass transmission temperature（Tg） of self-made hyperbranched polyurethane（HPU） and UV-curable hyperbranched polyurethane acrylate（HPUA） were analysised with thermogravimetric analyzer(TG) and differential scanning calorimeter(DSC).On this basis，the thermal decomposition mechanisms of HPU and HPUA were investigated with the combination of themogravimetric analyzer and Fourier transform infrared spectrometer（TG-FTIR）.The TG results demonstrated that HPU and HPUA had a simtlar thermal degration behavior，both presenting three thermal degration plateforms.Comparing the decomposition behaviors of two compounds under air and nitrogen，their decomposition behaviors were found to be similar，but the former was more quick.DSC analysis indicated that when adding HEA，the Tg of HPUA was obviously lower than that of HPU.TG-IR analysis demonstrated that，compared to that under nitrogen atmosphere，HPU and HPUA decomposed more rapidly and thoroughly under air.The thermal decomposition mechanism of HPU was degradations of alcohol，urethane bond and ureido bond，respectively，and the thermal decomposition mechanism of HPUA was decomposition of hydroxyethyl acrylate，urethane bonds and ureido bond，respectively. |
| Close |